Picture frame - Glazing - Data sheet

General properties

 

PLEXIGLAS® XT 0A000 (20070) or an equivelent standard – Solid sheet grade;
Largely UV absorbing (largely resistant) , will not fade or discolour over time
Conforms to BSI safety standard ISO 7823-2
Absolutely colourless and clear – Break-resistant to impact-resistant
Good resistance to diluted acids and to alkalis, limited resistance to organic solvents.
Max. service temperature approx. 70°c


Mechanical properties

 

Poisson’s ratio
(dilatation speed of 5 % per min; up to 2 % dilatation; at 23°c)

0.37

 Density

1.19

g/cm³

Impact strength

15

Kj/m2

Notched impact strength aiN   (lzod)

1.6

kJ/m2

Tensile strength

MPa

– 40 °C

100

MPa

23 °C

72

MPa

70 °C

35

MPa

Elongation at break

4.5

%

Flexural  strength
Standard test specimen
(80 x 10 x 4 mm3)

105

MPa

Compressive yield stress

103

MPa

Max.   safety stress
(up to 40 °C)

5

MPa

Modulus   of elasticity Et
(short-term value)

3300

MPa

Min. cold bending radius

330 x   thickness

Dynamic   shear modulus G

at approx. 10 Hz

1700

MPa

Indentation hardness H961/30

175

MPa

Abrasion   resistance in Taber abrader
test (100 rev.; 5,4 N; CS-10F)

20

%   Haze

Coefficient of friction
plastic / plastic

0.8

plastic / steel

0.5

steel / plastic

0.45

Resistance   to puck impact from
Thickness   (Test Certificate No. from FMPA Stuttgart)

12 mm

(46/900   549)


Thermal properties

 

 Coefficient   of linear thermal expansion for 0 – 50 °C

7

1/K

   (mm/m °C)

Possible expansion due to heat and moisture

5

mm/m

Thermal conductivity

0.19

W/mK

Specific heat c

1.47

J/gK

Forming temperature

150

°C

Max.   surface temperature
(IR radiator)

180

°C

Max. permanent service   temperature

70

°C

Reverse forming temperature

>   80;

°C

Ignition temperature

430

°C

Smoke gas volume

very   little

Smoke gas toxicity

none

Smoke gas corrosiveness

none

Class

B2

German  building inspectorate test report

P-K018

Vicat softening temperature

103

Heat   deflection temperature

under load (HDT)

deflection 1.8 MPa

95

deflection 0.45 MPa

100


Electrical properties

 

Volume resistivity

> 1015

Ohm · cm

Surface resistivity

5

Ohm

Dielectric strength Ed (1mm thickness)

~ 30

kV/mm

Dielectric  constant

at   50 Hz

3.7

at   0,1 MHz

2.8

Dissipation factor tan

at   50 Hz

0.06

Tracking,   CTI-Value

600


Optical properties

 

Transmittance D65

~ 92

UV transmission

No

Reflection loss the visible range (for each surface)

4

%

Total energy transmittance g

85

%

Adsorption in the visible range

<   0.05

%

Refractive index nD20

1.491


Behaviour towards water

 

Water absorption (24 hrs, 23 °C) from dry state;
specimen   60 x 60 x 2 mm3

38

Mg

Max. weight gain during immersion

2.1

%

Permeability   to

g   cm

cm2 h Pa

water vapour

2.3

N2

4.5

O2

2.0

CO2

1.1

air

8.3

 